Silica bricks for glass furnace refers to the silicon refractory product used in the high temperature part of the glass kiln (not in contact with the glass liquid), it is a kind of acid refractory mainly made from tridymite, cristobalite and a small amount of residual quartz as well as glass phase. The raw refractory material is natural silica sand whose SiO2 content should be more than 96%. The higher SiO2 content in silica sand, the higher temperature silica bricks resist.
Glass kiln silica brick has high temperature and volume stability, no pollution to glass liquid, chemical corrosion resistance, small bulk density, and can reduce the weight of furnace body.


Silica Bricks for Glass Melting Furnaces Feature

1.The high temperature volume is stable, and the furnace body does not change due to the temperature fluctuation surface. Because the silicon brick has a high load softening temperature and a small creep rate, the glass kiln can keep the furnace body from deforming at 1600 ° C, and the structure is stable.

2.No pollution to the glass liquid. The main component of silica brick is SiO2. If it is used, if there is any drop or surface droplet, silica bricks for glass melting furnace will not affect the quality of the glass liquid.

3.Resistance to chemical attack. The superstructure silicon brick is eroded by R2O gas in the glass batch, and a smooth metamorphic layer is formed on the surface, which makes the erosion speed lower and protects.

4. The bulk density is small, which can reduce the weight of the furnace body

Silica bricks are used in the roof and superstructure of glass melting tanks as well as for hot repairs.

PHYSICAL AND CHEMICAL SPECIFICATION

Silica brick for glass kiln BG-95 BG-96B BG-96A
SiO2           ≥ 95 96 96
Fe2O3          ≤ 1.2 1.0 0.8
 Flux index ≤ 0.7 0.6 0.5
0.2MPa refractoriness under load ≥ ℃

 

1660 1670 1680
Apparent porosity  % ≤ 22 22 22
Cold crushing strength MPa Unit weight <20kg ≥ 35 35 35
Unit weight ≥20kg ≥ 30 30 30
True density  g/cm3  2.35 2.34 2.34